ESPECIFICAÇÕES TÉCNICAS DE LIGAS FUNDIDAS |
|||||||||||||||
|
TIPOS |
COMPOSIÇÃO QUÍMICA |
PROPRIEDADES FÍSICAS |
SIMILARES |
||||||||||||
| %C | %SI | %Mn | %P | %S | %Cr | %Cu | %Mo |
LR Kgf/mm² |
LE Kgf/mm² |
ALG % |
DUREZA HB |
ATENDE ÀS NORMAS |
|||
|
|
|||||||||||||||
|
GG 15 |
3.50 3.70 |
2.20 2.40 |
0.60 0.80 |
0.30 Máx |
0.12 Máx |
|
|
|
|
15.0 Min |
6.7 Min |
|
150 180 |
|
ASTM A 48 CL 20/25 DIN 1691:GG 15 SAEJ 431C: GR2500 |
|
GG 20 |
3.30 3.50 |
2.00 2.20 |
0.60 0.80 |
0.25 Máx |
0.12 Máx |
|
|
|
20.0 Min |
8.1 Min |
|
170 200 |
ASTM A 48 CL 30 DIN 1691:GG 20 SAEJ 431 GR3000 |
||
|
GG 25 |
3.10 3.30 |
1.60 1.80 |
0.70 0.90 |
0.15 Máx |
0.10 Máx |
0.10 0.20* |
0.40 0.80* |
|
28.0 Min |
10.2 Min |
|
180 210 |
ASTM A 48 CL 35 DIN 1691:GG 25 SAEJ 431 GR3500 |
||
|
GG 30 |
2.90 3.10 |
1.40 1.60 |
0.80 1.00 |
0.10 Máx |
0.10 Máx |
0.10 0.20* |
0.40 0.80* |
|
36.0 Min |
14.0 Min |
|
210 240 |
ASTM A 48 CL 40 e 50 DIN 1691:GG 30 e 35 SAEJ 431 e GR4000 |
||
|
GG 40 |
2.80 3.00 |
1.40 1.60 |
0.80 1.00 |
0.10 Máx |
0.10 Máx |
0.10 0.40 |
0.75 1.50 |
0.30 0.60 |
41.0 Min |
31.6 Min |
|
220 250 |
ASTM A 48 CL 55 e 60 DIN 1691:GG 40
|
||
|
GGG 40 |
3.50 3.90 |
2.60 2.90 |
0.20 Máx |
0.04 Máx |
0.02 Máx |
|
|
|
42.2 Min |
28.1 Min |
18.0 Min |
140 170 |
ASTM A 395 GR60/40/18 e 6545-12 DIN 1693:GGG 40 |
||
|
GGG 50 |
3.50 3.90 |
2.50 2.80 |
0.20 Máx |
0.06 Máx |
0.02 Máx |
|
0.30 0.40 |
|
56.3 Min |
38.5 Min |
6.0 Min |
180 220 |
ASTM A 536 GR 80/55/06 DIN 1693:GGG 50 |
||
|
GGG 60 |
3.50 3.90 |
2.50 2.80 |
0.20 Máx |
0.06 Máx |
0.02 Máx |
|
0.50 0.60 |
|
60.0 Min |
98.0 Min |
3.0 Min |
230 260 |
DIN 1691:GGG 60
|
||
|
GGG 70 |
3.50 3.90 |
2.50 2.80 |
0.20 Máx |
0.06 Máx |
0.02 Máx |
|
0.70 0.80 |
|
70.3 Min |
49.2 Min |
3.0 Min |
240 300 |
ASTM A 536 GR 100/70/30 DIN 1693:GGG 70 |
||
|
|
|||||||||||||||
|
|
|
|
|
|||||||||||
|
GGG FUNDIDO NODULAR GG FUNDIDO CINZENTO |
|
|
|
|
|||||||||||